What We Do

Product range:
  • Wire Rod 5.5 mm to 16.0 mm
  • Rebar In Coil - 6 mm to 16 mm
  • Rebar Straight - 10 mm to 40 mm
Coil weight:
  • 2000 kg nominal
Rebar bundle weight:
  • From 1000 kg 6 m long bars
  • From 2000 kg 12 m long bars
  • From 3000 kg 20 m long bars

Steel Grades: B500B BS4449 - 05

This British Standard specifies requirements for ribbed weldable reinforcing steel used for the reinforcement of concrete structures.
The standard covers steel delivered in the form of bars, coils and decoiled products.

Chemical composition(maximum % by mass):
Grade No. Carbon Sulphur Phosphorus Nitrogen Copper Carbon equivalent
B500B 0.22 0.05 0.05 0.012 0.80 0.50
Mechanical properties:

Yield strength, Re
MPa
Tensile/yield strength ratio, Rm/Re Total elongation at maximum force, Agt
%
B500B 500 1.08 5.0
Grade B500B: bars shall have two or more series of parallel transverse ribs.
For bars with two or three rib series, one of the series shall be at a contrary angle to the others and for bars with four rib series, two of the series shall be at a contrary angle to the others.

An example of rib pattern of grade B500B with four transverse rib series is given below:




SAE1006 – 1018 ASTM A510M – 06

This specification covers general requirements for carbon steel wire rods and uncoated coarse round wire in coils or straightened and cut lengths.

Chemical Composition Limits, %
Grade No. Carbon Manganese Phosphorus, max Sulfur, max
1006 0.08 max 0.25 to 0.45 0.040 0.050
1008 0.10 max 0.30 to 0.50 0.040 0.050
1010 0.08 to 0.13 0.30 to 0.60 0.040 0.050
1011 0.08 to 0.13 0.60 to 0.90 0.040 0.050
1012 0.10 to 0.15 0.30 to 0.60 0.040 0.050
1013 0.11 to 0.16 0.50 to 0.80 0.040 0.050
1015 0.13 to 0.18 0.30 to 0.60 0.040 0.050
1016 0.13 to 0.18 0.60 to 0.90 0.040 0.050
1017 0.15 to 0.20 0.30 to 0.60 0.040 0.050
1018 0.15 to 0.20 0.60 to 0.90 0.040 0.050
Mechanical properties as per contract.

Raw materials. Type of steel billets. Our Billet Store

Countries of origin: UAE, Sultanate of Oman, Kingdom of Bahrain and Ukraine
Our billet store capacity: 100,000 t
Billets dimension: 150mmx150mmx12M

Steel Grades: SAE1006, SAE1008 SAE1012 SAE1018, B500B BS4449 - 2005

Furnace (furnace details)

Walking Beam Furnace
Discharging temperature (surface) 1,150°C
Load capacity 175t/h

Production line. Advantages

Number of stands:
  • Wire Rod 27 stands
  • Rebar in Coil 27 stands
  • Rebar Straight 17 stands
Rolling Speed:
  • Line 1
    • 105 m/s - Wire Rod
    • 70 m/s - Rebar in Coil
  • Line 2
    • 16 m/s - Rebar Straight
Cooling bed length - 120m

Length of coil cooling conveyer 91m.
Capacity: up to 2 hot coils depending on Stelmor speed.

The plant produces bar and wire rod products for civil construction. The rolling mill project was designed in 2005 by Germany’s concern SIEMENS - VAI ( SVAI ). Our mill capacity is 1.1 MTPA producing wire rods and rebars.

1. Rebar N216 (Hot test), Wire SAE 1006 Φ5,5 MM

%
C Mn P S Si Cr Ni Cu AI N
Min Max Min Max Max Max Min Max Max Max Max Max Max
Wire
ASTM A 510 M
SAE 1006 USI 0,05 0,08 0,25 0,40 0,015 0,010 0,10 0,20 0,10 0,10 0,10 0,02 0,008

2. Wire SAE 1008 Φ5,5 Φ6,5 MM

%
C Mn P S Si Cr Ni Cu AI N
Min Max Min Max Max Max Min Max Max Max Max Max Max
Wire
ASTM A 510 M
SAE 1008 USI 0,05 0,10 0,25 0,30 0,015 0,010 0,10 0,20 0,10 0,10 0,10 0,02 0,008

3. Wire SAE 1012 Φ7,0 MM

%
C Mn P S Si Cr Ni Cu AI N
Min Max Min Max Max Max Min Max Max Max Max Max Max
Wire
ASTM A 510 M
SAE 1012 USI 0,10 0,15 0,30 0,60 0,015 0,010 0,10 0,20 0,10 0,10 0,10 0,02 0,008

4. BS 4449 rebar N216

%
C Mn P S Si Cr Ni Cu N Carbon Equivalent Crg
Min Max Min Max Max Max Min Max Max Max Max Max Max
Rebar
N216
BS 4449
Grade
B500A
USI 0,19 0,22 0,10 0,30 0,015 0,010 0,20 0,40 0,15 0,10 0,10 0,008 0,50